Investigation of corrosion properties of box boring din 20MnCr5 steel bars
E3S Web of Conferences · Temmuz 2023
Makale Bilgileri
DergiE3S Web of Conferences
Yayın TarihiTemmuz 2023
Cilt / Sayfa401
Scopus ID2-s2.0-85169679844
Erişim🔓 Açık Erişim
Özet
In this study, boriding process was carried out on ∅ 11 mm diameter DIN 20MnCr5 quality steel bars, used in chain elements such as links and rings, and fasteners such as bolts, at 950oC boronizing temperature, boriding times of 2.5 and 7.5 hours. In this study, the formation and growth of the boride layer and the metallographic structure, the coating thickness and corrosion properties of the boronized steels were investigated depending on the boriding conditions. In the box boriding process, Ekabor-II powder mixture, with its commercial name, was used as boriding powder. According to the optical microstructure results made as a result of box boriding, the coating thickness was 371.5 μm in the ∅ 11 mm diameter boronized DIN 20MnCr5 steel bar for 7.5 hours boriding times while it was 195.6 ?m in that steel bar for 2.5 hours boriding times. Corrosion experiments were carried out in solutions prepared by adding 3.5% NaCl to distilled water. According to the results of the immersion test, the lowest corrosion rate in mdd was measured as 112 mg/(dm2 x day) in the ∅ 11 mm diameter, 7.5 hour boronized sample, and the highest corrosion rate in mdd was 1456.75 mg/(dm2 x day) in the untreated ∅ 11mm diameter sample. In the potentiodynamic polarization test, parallel results were obtained for immersion corrosion. Corrosion rate values (icor) were measured at the highest value of 209 x 10- 6 A/cm2 in the untreated ∅ 11 diameter sample, while the lowest icor value was 0.0039 x 10- 6 A/cm2 in the ∅ 11 mm diameter sample borided for 7.5 hours.
Yazarlar (6)
1
Nurullah Şahin
2
Aysun Işikgül
3
Umida Ziyamukhamedova
4
Hayrettin Ahlatcı
5
Mustafa Acarer
6
Mucahit Sevim
Kurumlar
Karabük Üniversitesi
Karabuk Turkey
Kardemir Iron and Steel Co.
Karabuk Turkey
Selçuk Üniversitesi
Selçuklu Turkey
Tashkent State Transport University
Tashkent Uzbekistan