Effect of Cr particulate reinforcements in different ratios on wear performance and mechanical properties of Cu matrix composites
Journal of the Brazilian Society of Mechanical Sciences and Engineering · Nisan 2018
YÖKSİS Kayıtları
Effect of Cr particulate reinforcements in different ratios on wear performance and mechanical properties of Cu matrix composites
Journal of the Brazilian Society of Mechanical Sciences and Engineering · 2018 SCI
Dr. Öğr. Üyesi ÜSAME ALİ USCA →
YÖKSİS Kayıtları — ISSN Eşleşmesi
Effect of Cr particulate reinforcements in different ratios on wear performance and mechanical properties of Cu matrix composites
2018 ISSN: 1678-5878 SCI
Dr. Öğr. Üyesi ÜSAME ALİ USCA →
Experimental investigation of the cetane improver and bioethanol addition for the use of waste cooking oil biodiesel as an alternative fuel in diesel engines
2020 ISSN: 1678-5878 SCI-Expanded
Prof. Dr. İLKER ÖRS →
Machining and optimization of reinforced copper composites using different cooling-lubrication conditions
2022 ISSN: 1678-5878 SCI-Expanded Q3
Dr. Öğr. Üyesi ÜSAME ALİ USCA →
Impact of boron nitride and silicon carbide on tribological properties of Al-3Gr-based hybrid composites
2023 ISSN: 1678-5878 SCI-Expanded Q3
Dr. Öğr. Üyesi ÜSAME ALİ USCA →
Assessment of the machinability and energy consumption characteristics of Cu–6Gr hybrid composites under sustainable operating
2024 ISSN: 1678-5878 SCI-Expanded Q3
Dr. Öğr. Üyesi ÜSAME ALİ USCA →
Finite element analysis and statistical investigation of S960ql structure steel machinability with milling method
2024 ISSN: 1678-5878 SSCI
Prof. Dr. SÜLEYMAN NEŞELİ →
Makale Bilgileri
ISSN16785878
Yayın TarihiNisan 2018
Cilt / Sayfa40
Scopus ID2-s2.0-85044200357
Özet
The aim of this study was to determine the effect of different ratios Cr particle reinforcement on the hardness and wear resistance of Cu matrix composites produced by using (P/M) method. Cr particles were added at different weight ratios of 5, 10 and 15%, in pure Cu dust. The prepared mixtures were shaped under a pressure of 400 MPa. The shaped pieces were sintered at 900 °C for 30 min. The success of the sintering process was evaluated by examining the intensity and SEM images. Microscope studies were performed using scanning electron microscopy (SEM). Hardness measurement method was used for determining hardness. In the SEM analysis, it was observed that the Cr phase was uniformly distributed in the Cu matrix composed of coaxial grains. In addition, an increase in the hardness was observed depending on the increase in the Cr ratio. The wear behaviors of the composite materials produced were investigated by pin-on-disk wear test. As the disk, a surface-hardened AISI 1050 steel was used. As a result of this examination, composite materials; depth of wear, losses in the weight, variation of friction coefficient, variation of wear diameters at 0.4 m/s shear rate and 1500 m shear distance were investigated by applying 50 N and 75 N loads. As a result of these investigations, it has been found that as the Cr particle reinforcement ratio in the Cu matrix composites increases, hardness and the wear resistance were increased positively.
Yazarlar (2)
1
Mahir Uzun
ORCID: 0000-0002-0907-6875
2
Üsame Ali Usca
Anahtar Kelimeler
Chromium
Composite
Copper
Hardness
Sintering
Wear
Kurumlar
Bingöl Üniversitesi
Bingol Turkey
Scimago Dergi (ISSN Eşleşmesi)
Journal of the Brazilian Society of Mechanical Sciences and Engineering
Q2
OA
SJR Skoru0,466
H-Index67
YayıncıSpringer Verlag
ÜlkeGermany
Aerospace Engineering (Q2)
Applied Mathematics (Q2)
Automotive Engineering (Q2)
Engineering (miscellaneous) (Q2)
Industrial and Manufacturing Engineering (Q2)
Mechanical Engineering (Q2)
Metrikler
40
Atıf
2
Yazar
6
Anahtar Kelime