Effect of hybridization and stacking sequence on damage development in AWJ machining of Al/FRP/Al FML composites
Journal of Manufacturing Processes · Aralık 2024
YÖKSİS Kayıtları
Effect of hybridization and stacking sequence on damage development in AWJ machining of Al/FRP/Al FML composites
Journal of Manufacturing Processes · 2024 SCI-Expanded
DOÇENT ŞAKİR YAZMAN →
Makale Bilgileri
DergiJournal of Manufacturing Processes
Yayın TarihiAralık 2024
Cilt / Sayfa131 · 141-159
Scopus ID2-s2.0-85203407375
Özet
In this study, 5 different Al2024/FRP/Al2024 metal stacked composites were produced and their machinability by abrasive water jet machining (AWJM) method was investigated. Synergistic interaction of these materials offers new and improved properties, but machinability remains an area of research due to widely varying mechanical properties. The effects of different stacking and traverse speed on hole quality in cutting with AWJM were determined. The hole diameter deviation (HDD) ratio, kerf, delamination, hole circularity, and surface morphology were analyzed. Result of the current study showed that the increase in traverse speed caused an increase in the HDD ratio, in the visibility of the cutting starting point, in the deviation of circularity, and in the bore-hole damage formation. In all stacks with CFRP, an average deviation of 5 % at the hole entrance and 4 % at the hole exit occurred at a traverse speed of 1000 mm/min. At 400 and 600 mm/min traverse speeds, an average of 2.8 % deviation occurred at the hole entrance and an average of 2.13 % at the hole exit. This proves that the traverse speed has a significant effect on the hole diameter. In addition, as the traverse speed decreased, it was noticed that the layers separated from each other, causing delamination, and therefore the thickness of the FML increased. Different defects were observed to occur in FRP structures used in FML with SEM analysis. Intralayer defects were more dominant in GFRP laminate, whereas interlayer defects were found to form in CFRP laminate.
Yazarlar (5)
1
Mehmet Akif Doğan
2
Lokman Gemi
3
Şakir Yazman
4
Ferhat Ceritbinmez
5
Ahmet Yapici
Anahtar Kelimeler
AWJM
Damage mechanics
Delamination
Hybrid
Stacking sequence
Kurumlar
Iskenderun Technical University
Iskenderun Turkey
Manufacturing-Research and Development
Eskisehir Turkey
Necmettin Erbakan Üniversitesi
Meram Turkey
Recep Tayyip Erdogan University
Rize Turkey
Selçuk Üniversitesi
Selçuklu Turkey
Metrikler
15
Atıf
5
Yazar
5
Anahtar Kelime