Achieving adhesion between resin cement and zirconia requires pretreatment of the surface. This in vitro study aimed to evaluate the effect of femtosecond laser beam angle and the shape of the formed surfaces, on the roughness and shear bond strength (SBS) of resin cement to zirconia ceramic. Seventy Y-TZP ceramic specimens were divided into seven groups (n = 10). A femtosecond laser irradiation was performed on the ceramic surface of three shapes (spiral (SP), square (SQ) and circular (CI) and at two angles (30 and 90°) to give SP-30, SQ-30 and CI-30 and SP-90, SQ-90 and CI-90, respectively. After treatment, the surface roughness of all specimens was evaluated using a profilometer. One specimen from each group was analysed using a scanning electron microscope. The bonded specimens were thermocycled 5000 times and then an SBS test was performed. Kruskal-Wallis and Mann-Whitney U tests were used to analyse surface roughness and SBS values. The control group had statistically lower surface roughness (Ra) values than the treated groups (p < 0.05). SP-30 and SQ-30 laser treated specimens showed higher Ra values than the other specimens. Statistically significant SBS values (p = 0.000) were observed between the groups. All laser treated samples showed greater SBS compared to the control group. SP-30, SQ-30 and SQ-90 groups showed the highest SBS values. Within the limitations of this experimental study, the highest mean values for Ra and SBS were achieved with SP and SQ surfaces using a 30° angle laser beam.